appendix 4
HARDNESS
(
SHORE A)
TENSILE
PSI
ULTIMATE
ELONGATION
%
TEAR
RESISTANCE
LBS/IN.
DIN
ABRASION
HEAT AGING
OIL RESISTANCE
(
OIL NO3)
TEMPERATURE
RANGE
MULLEN
BURST
1
PLY PSI
AB-613
80
700
min.
150
min.
94
hrs @ 70°C
Changed
Tensile: -25% max
Elongation: -25% max
-20
° to 200°F
(-29
° to 93°C)
AB-617
80
500
min.
100
min.
70
hrs. @ 70°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
-20
° to 180°F
(-29
° to 82°C)
IM-618
75
400
nom.
220
nom.
-20
° to 180°F
(-29
° to 82°C)
AB-619
75
600
min.
100
min.
70
hrs. @ 70°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
-20
° to 180°F
(-29
° to 82°C)
SECTION 3 : NEOPRENE
AB-250
50
600
min.
300
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
70
hrs @ 100°C
Volume changed: 120%
max.
-20
° to 190°F
(-29
° to 88°C)
AB-260
60
600
min.
300
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
70
hrs @ 100°C
Volume changed: 120%
max.
-20
° to 190°F
(-29
° to 88°C)
AB-270
70
600
min.
200
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
70
hrs @ 100°C
Volume changed: 120%
max.
-20
° to 190°F
(-29
° to 88°C)
IM-252
50
500
nom.
300
nom.
-20
° to 190°F
(-29
° to 88°C)
Page 2 of 10 // 7069-E (23-01-2013)