appendix 4
HARDNESS
(
SHORE A)
TENSILE
PSI
ULTIMATE
ELONGATION
%
TEAR
RESISTANCE
LBS/IN.
DIN
ABRASION
HEAT AGING
OIL RESISTANCE
(
OIL NO3)
TEMPERATURE
RANGE
MULLEN
BURST
1
PLY PSI
AB-263
60
900
min.
300
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: -15% max
Elongation: -40% max.
70
hrs. @ 100°C
Changed
Tensile: -60% max.
Elongation: -50% max
Volume: 100% max.
-20
° to 190°F
(-29
° to 88°C)
AB-273
70
1000
min.
200
min.
70
hrs. @ 100°C
Changed
Hardness: ±15 points max.
Tensile: -15% max
Elongation: -40% max.
70
hrs. @ 100°C
Changed
Tensile: -60% max.
Elongation: -50% max
Volume: 100% max.
-20
° to 190°F
(-29
° to 88°C)
AB-289
80
1000
min.
100
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
70
hrs @ 100°C
Volume changed: 120%
max.
-20
° to 190°F
(-29
° to 88°C)
SECTION 4 : NITRILE
AB-344
40
1000
min.
500
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
70
hrs @ 100°C
Volume changed: 80%
max.
-20
° to 190°F
(-29
° to 88°C)
AB-364
60
1000
min.
350
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
70
hrs @ 100°C
Volume changed: 80%
max.
-30
° to 190°F
(-34
° to 88°C)
AB-355
50
2000
min.
350
min.
70
hrs @ 100°C
Changed
Hardness: ±15 points max.
Tensile: ±30% max
Elongation: -50% max.
70
hrs. @ 100°C
Changed
Hardness: -10 to +5
points max.
Tensile: -45% max.
Elongation: -45% max
Volume: 0 to 25% max
-40
° to 200°F
(-40
° to 93°C)
Page 4 of 10 // 7069-E (29-08-2012)