appendix 4
HARDNESS
(
SHORE A)
TENSILE
PSI
ULTIMATE
ELONGATION
%
TEAR
RESISTANCE
LBS/IN.
DIN
ABRASION
HEAT AGING
OIL RESISTANCE
(
OIL NO3)
TEMPERATURE
RANGE
MULLEN
BURST
1
PLY PSI
TG-65
TRANSEAL
65
2400
500
3
weeks @ 120°C
Changed
Hardness: 18 points
Tensile: 2%
Elongation: -66%
(
all values nom.)
4
weeks @ 125°C
Voltesso 35 Oil
Changed
Hardness: 3 points
Tensile: -60%
Elongation: -78%
Mass: 10%
Volume: 12%
(
all values nom.)
-20
° to 200°F
(-29
° to 93°C)
AB-168
60
2250
min.
450
min.
168
hrs. @ 70°C
Changed
Hardness: +10 points max.
Tensile: -25% max.
Elongation: -25% max..
AB-258
50
2250
min.
400
min.
70
hrs. @ 100°C
Changed
Hardness: +15 points
Tensile: -15% max.
Elongation: -40% max.
AB-268
60
2250
min.
350
min.
70
hrs. @ 100°C
Changed
Hardness: +15 points
Tensile: -15% max.
Elongation: -40% max.
AB-278
70
2250
min.
300
min.
70
hrs. @ 100°C
Changed
Hardness: +15 points
Tensile: -15% max.
Elongation: -40% max.
MIL-
PRF-1149
type 1,
class 1
50
1000
min.
300
min.
94
hrs @ 70°C
Changed
Hardness: 10 points max.
Tensile: -20% max
Elongation: -35% max.
70
hrs @ 100°C
Volume changed: 120%
max.
Page 9 of 10 // 7069-E (23-01-2013)